Thermosetting Polyester Commercial RAL9005 Sandy Powder Coating
Black Color
Average coating rate
A. Smooth Surface:
6-12/KG, film thickness 60μm (calculated according to 100 consuming
of powder coating)
B. Texture Surface:
5-7/KG,film thickness is about 80-120μm
Powder coating is a process of coating metal with a thermosetting
finish applied in powder form and baked to a oven to bond it to the
metal surface. Powder coating has many advantages over traditional
liquid coating: It's better for the environment, applies thicker
without running, and is easy to style with. Although certain
aspects of powder coating can be tricky, it's certainly not
difficult, especially for an enterprising soul. Proper cleaning and
tools can be the difference between an amateur and a good powder
coating job.
Product series
The products include high light ( above 86%),
glazed (76%-85%),
matt(20%-50%),
super matt (below 20%).
We also offer a variety of shiny products according to the needs of
users.
Health and safety:
This product is non-toxic. In the course of inhalation of dust
should be avoided. The operators should wear appropriate dust mask
and glasses.
Application
Suitable for all kinds of products such as household appliances,
instruments, meters medical devices,
automotive components, metal furniture, fitness equipment, indoor
decorative painting, etc.
Also apply to a variety of equipment, pipes, pipe fittings and
other requirements of corrosion coating.
Storage requirements:
Store below 30 °C, ventilated, dry, clean room, not near the fire,
heat, direct sunlight, open dumps is prohibited.Under this
condition, the powder can be stable for 12 months, more than the
storage period may be re-examined, such as the results meet the
requirements, can still be used.
Technic Data:
| pplication Field | Apply to anticorrosive and insulative products: |
| Anticorrosion pipeline,rebar,bridge,steel structure, |
| pylon,tank,marine fittings,electric control cabinet, |
| switch components,lighting sets. |
| Application Condition | Electrostatic spray/Triboelectric gun spray. |
| Recommended curing condition:200 degree centigrade for 12 minutes |
| (object surface temperature),range from 190 degree centigrade |
| for 20 minutes to 210 degree centigrade for 8minutes. |
| Recommended film thickness:50~80um, range from 40~150um |
| Physical Property | Specific gravity | 1.4~1.8g/cm3 as per formula and color |
| Particle size | average 35~40um |
| Test Condition | Substrate | 0.5mm thickness cold rolled steel sheet |
| Pretreatment | Remove rust and grease |
| Film thickness | 50~80um |
| Curing temperature | 200 degree centigrade for 12 minutes |
| Mechanical Property | Pencil hardness | ISO 15184:1998,2H |
| Adhesion (by griding) | GB/T 9286-1998,0grade |
| Impact test | GB/T 1732-1993,≥50 kg.cm |
| Bending test | GB/T 6742 ,≤2mm |
| Cupping test | GB/T 9753,≥7mm |
| Chemical and Durability Test | Salt spray test | GB/T 1771,≥1000 hours,no obvious change , |
| crossion width at cross≤2mm |
| Heat and moisture test | GB/T 1740,≥1000 hours,no change |